Hot Ramming Paste UsingThe invention relates to a hot ramming paste crushing method for aluminum electrolytic cell, which includes the following steps:(1) The
Hot Ramming Paste Using
The invention relates to a hot ramming paste crushing method for aluminum electrolytic cell, which includes the following steps:
(1) The hot ramming paste is hung into the heating furnace for heating, a temperature controller is installed in the heating furnace, and the temperature is set at 50℃;
(2) When the ambient temperature in the furnace reaches 50℃, it is kept at a constant temperature for 5-8 hours;
(3) After the initial heating time is enough, the paste is hoisted out, and its gravitational potential energy is used to fall from the air in the form of free fall onto the base of the steel strip teeth；
(4) Finally, the paste is put into the kneading pot and heated to the construction temperature of 110±10℃. The invention can not only reduce labor input, protect the essence of the material, prolong the service life of the equipment, but also ensure the service performance of the paste and prolong the service life of the electrolytic cell。
-
Article Tags:
Hot Ramming Paste
www.chinaelectrodes.
2022-03-23 01:58:10Generally, when the cathode carbon block is lower than its roasting temperature, it shows a positive coefficient of thermal expansion as the temperature increases, while the ramming paste will shrink from curing temperature to the maximum roasting temper
www.chinaelectrodes.
2022-03-21 03:57:32From 1954 to 1976, calcined petroleum was widely used in aluminum plants. On the one hand, the carbon plant of aluminum factory produces anode paste, using local materials; On the other hand, there were no more effective pastes.
www.chinaelectrodes.
2022-03-19 13:55:29An important index to measure the performance of calcined pet coke is the content of volatiles in calcined pet coke. If the content of volatiles in calcined pet coke is too high, the shrinkage ratio of raw anode will be large in the roasting process, and